Research on High- and Low-Temperature Rheological Properties of High-Viscosity Modified Asphalt Binder

This study evaluates the critical high- and low-temperature rheological properties of a high-viscosity modified asphalt (HVMA) binder by analyzing one neat and three high-viscosity modified binders (B-type, Y-type, and H-type) using temperature sweep tests and multi-stress creep recovery tests (MSCR) through the dynamic shear rheometer (DSR), and low-temperature creep stiffness properties by the bending beam rheometer (BBR). Technical indexes such as the softening point temperature, dynamic viscosity, rutting factor, unrecoverable creep compliance, and the creep recovery rate are measured and calculated for high-temperature properties, while the m/S value, dissipation energy ratio, relaxation time, elongation, creep stiffness, and creep speed are used as technical indexes for low-temperature properties. The results show that the incorporation of high-viscosity modifiers reduces the unrecoverable creep compliance and increases the creep recovery rate of the asphalt binder. Non-recoverable creep compliance is found to be a reliable indicator for high-temperature performance, while at low temperatures, the relaxation time decreases, the dissipation energy increases, and the stress relaxation ability improves. The dissipation energy ratio and m/S value are suggested to evaluate the low-temperature performance of HVMA binders using the Burgers model based on the BBR bending creep stiffness test. Therefore, this study recommends using the unrecoverable creep compliance via MSCR to evaluate high-temperature properties and dissipation energy ratio and m/S value for low-temperature properties in the evaluation of HVMA binders.

This creative work has been published under the Creative Commons Attribution 4.0 International (CC-BY 4.0) license which allows copying, and redistribution as well as adaptation of the original work provided appropriate credit is given to the original author and the conditions of the license are met.