Effects of GO/Al2O3 and Al2O3 Nanoparticles on Concrete Durability against High Temperature, Freeze-Thaw Cycles, and Acidic Environments

In this paper, the effect of GO/Al2O3 and Al2O3 synthesized nanoparticles on the durability of concrete is studied. To this end, after the synthesis of nanoparticles and confirmation of nanoparticles fabrication by SEM and FT-IR spectra, three concrete samples for each experiment related to each mix design were prepared and subjected to freeze-thaw cycles, high temperature, and acidic environment. The results show that the samples containing GO/Al2O3 nanoparticles had the least weight loss in freeze-thaw cycles as well as better resistance against acidic environment and the lowest apparent changes at high temperature compared to the samples containing nano-Al2O3 and the samples without nanoparticles. The replacement of 2 wt.% of cement with GO/Al2O3 nanoparticles results in the highest increase in concrete durability. The presence of nanoparticles in the concrete microstructure and the validation of the results are investigated by FT-IR, SEM, and EDX spectra.

This creative work has been published under the Creative Commons Attribution 4.0 International (CC-BY 4.0) license which allows copying, and redistribution as well as adaptation of the original work provided appropriate credit is given to the original author and the conditions of the license are met.